摘要：Flexible interfaces between Si anodes and composite electrolytes consisting of poly(propylene carbonates) (PPCs) and garnets have been fabricated. The solid polymer electrolytes (SPEs) of PPC/garnet/LiTFSI show the conductivity of 4.2 × 10−4 S cm−1 at room temperature. Their combination with the Si layer anodes allows great alleviation of internal stress resulting from the large volume variation during lithiation and delithiation process of Si anodes. As a result, the Si/SPE/Li cells exhibit 2520 mAh g−1, 2260 mAh g−1, 1902 mAh g−1, 1342 mAh g−1 at 0.1 C, 0.2 C, 0.5 C, and 1 C, respectively. Furthermore, with such compatible and stable interfaces of Si/SPE and the LiFePO4 cathodes in solid-state batteries, the specific capacity of 2296 mAh g−1 in terms of Si is obtained, which remains 82.6% after 100 cycles at room temperature and 0.1 C. The results here indicate that constructing of flexible interfaces between Si anodes and SPEs is a promising strategy to develop high performance solid-state batteries.

论文类型：期刊论文

是否译文：否

发表时间：2018-04-15

发布期刊链接：https://www.sciencedirect.com/science/article/abs/pii/S037877531830140X